A36/Q235/S235JR Carbon Steel Plate Description
The chemical composition of A36 steel plate is mainly composed of iron, carbon, silicon, manganese, phosphorus, sulfur and other elements. Among them, iron is the most important component, accounting for more than 99% of the entire chemical composition. The carbon content is relatively high, generally around 0.2%, ensuring that the steel has a certain hardness and toughness. The addition of silicon, manganese and other elements enhances the strength and toughness of steel. The content of elements such as phosphorus and sulfur is low to ensure that the steel plate has good welding performance and corrosion resistance. A36 steel plate has excellent mechanical properties, and its tensile strength, yield strength, elongation and impact toughness are all higher than ordinary steel.
Parámetros del producto
| Nombre del producto | Placa de acero al carbono A36/Q235/S235JR |
| Production Process | Hot Rolling, Cold Rolling |
| Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
| Anchura | 100mm-3000mm |
| Longitud | 1m-12m, or Customized Size |
| Espesor | 0.1mm-400mm |
| Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
| Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| C | Cu | Fe | Mn | P | Si | S |
| 0.25~0.290 | 0.20 | 98.0 | 1.03 | 0.040 | 0.280 | 0.050 |
Mechanical Properties
| A36 | Limit Tensile Strength | Tensile Strength,
Límite elástico |
Elongation at Break
(Unit: 200mm) |
Elongation at Break
(Unit: 50mm) |
Modulus of Elasticity | Bulk Modulus
(Typical for Steel) |
Poisson’s Ratio | Shear Modulus |
| Metric | 400~550 MPa | 250 MPa | 20.0% | 23.0 % | 200 GPa | 140 GPa | 0.260 | 79.3 GPa |
| Imperial | 58000~79800 psi | 36300 psi | 20.0% | 23.0 % | 29000 ksi | 20300 ksi | 0.260 | 11500 ksi |
Physical Performance
| Physical Performance | Metric | Imperial |
| Density | 7.85 g/cm3 | 0.284 lb/in3 |
Scope of Application
Bolted, riveted or welded structures for bridges, buildings and oil drilling rigs.
Used for forming storage tanks, silos, bearing plates, fixtures, rings, templates, fixtures, sprockets, cams, gears, bottom plates, forgings, decoration engineering, piles, brackets, automobiles and agricultural equipment, frames, mechanical parts, etc.
Equivalent Material
| National Standard GB | European Standard EN | American Standard ASTM | German Standard DIN, WNr | Japanese Standard JIS | French Standard AFNOR | British Standard BS | Canada HG |
| Q235B | S235JR | A283C | St37-2 | SM400A | E24-2 | 40A/40B | 230G |
| Italy UNI | India IS | Switzerland SS | Australia ONORM | Norway NS | Spain UNE | International Standards ISO | Portugal NP |
| Fe360B | IS2062 | 1311/1312 | RSt360B | NS12123 | AE235B-FN | E235B / Fe360B | FE360-B |