HRB600 High Strength Hot Rolled Reinforced Bar Description
HRB600 is a high-strength steel bar with a standard yield strength of 600MPa, hence it is also known as 600MPa grade high-strength steel bar. This type of steel reinforcement has been widely used in modern buildings and engineering structures, especially in situations where there is a need to improve structural performance and save materials.
Product Parameters
| Product Name | HRB600 High Strength Hot Rolled Reinforced Bar | |||
| Standard | EN/DIN/JIS/ASTM/BS/ASME/AISI, etc. | |||
| Common Round Bar Specifications | 3.0-50.8 mm, Over 50.8-300mm | |||
| Flat Steel Common Specifications | 6.35×12.7mm, 6.35×25.4mm, 12.7×25.4mm | |||
| Hexagon Bar Common Specifications | AF5.8mm-17mm | |||
| Square Bar Common Specifications | AF2mm-14mm, AF6.35mm, 9.5mm, 12.7mm, 15.98mm, 19.0mm, 25.4mm | |||
| Length | 1-6meters, Size Accept Custom | |||
| Diameter(mm) | Hot Rolling Round Bar | 25-600 | Cold Rolling Square Bar | 6-50.8 |
| Hot Rolling Square Bar | 21-54 | Cold Rolling Hexagon Bar | 9.5-65 | |
| Cold Rolling Round bar | 6-101.6 | Forged Rebar | 200-1000 | |
| Surface Process | Bright, Polished, Black | |||
| Other Services | Machining(cnc), Centerless Grinding(cg), Heat Treatment, Annealing, Pickling, Polishing, Rolling, Forging, Cutting, Bending, Small Machining, etc. | |||
Chemical Composition
| Carbon | Silicon | Manganese | Sulphur | Phosphorus |
| 0.25% | 0.80% | 1.6% | 0.045% | 0.045% |
Mechanical Properties
| Chinese Rebar Code | Yield Strength (Mpa） | Tensile Strength (Mpa） | Carbon Content |
| HRB400, HRBF400, HRB400E, HRBF400E | 400 | 540 | ≤0.25 |
| HRB500, HRBF500, HRB500E, HRBF500E | 500 | 630 | ≤0.25 |
| HRB600 | 600 | 730 | ≤ 0.28 |
Scope of Application
Widely used in houses, bridges, roads, especially railways and other civil engineering.